OEM, ODM 96% alumina, zirconia ,cordierite Ceramic Substrates (0.8mm) manufacturing - Product
Place of Origin : Shanghai,China
Delivery Time : 7-20 Days
Product Description
OEM, ODM 96% alumina, zirconia ,cordierite Ceramic Substrates (0.8mm) manufacturing Material : 96% Alumina Ceramic Substrates/Ceramic Plate
Thickness:0.8mm
We manufactures custom technical ceramic parts and components ,covering a wide range of customer reuquirements .We make use of several forming and machining techniques to process components made from alumina, zirconia ,cordierite .These materials may be used in applications that require wear or coorosion resistance .high temperature
Physical Specification
Other Specification : OEM, ODM 96% Alumina, Zirconia ,cordierite Ceramic Substrates (0.8mm) Manufacturing Material : 96% Alumina Ceramic Substrates/Ceramic Plate
Thickness:0.8mm
We Manufactures Custom Technical Ceramic Parts And Components ,covering A Wide Range Of Customer Reuquirements .We Make Use Of Several Forming And Machining Techniques To Process Components Made From Alumina, Zirconia ,cordierite .These Materials May Be Used In Applications That Require Wear Or Coorosion Resistance .high Temperature Capability ,or Ceramic Insulators For Electrical Resistance.
- - - -
Name | Unit | Alumina | Zirconia |
Content | % | 95 | 99 | 99.7 | 94 |
Density | G/cm3 | 3.65 | 3.80 | 3.90 | 6.00 |
Hardness(Hv0.5) | GPa | 13.1 | 15.0 | 17.1 | 13.2 |
Flexural Strength | MPa | 340 | 310 | 370 | 1000 |
Elasticity | GPa | 300 | 330 | 350 | 200 |
Poisson's Ratio | | 0.23 | 0.23 | 0.23 | 0.30 |
Max Tem. | C | 1400 | 1750 | 1800 | 1050 |
Heat Expansion | 10-6/C(40-800C) | 7.8 | 8.0 | 8.0 | 11.0 |
Thermo Conductivity | W/mK(20C) | 22 | 28 | 31 | 2.6 |
Thermal Resistance | C | 200 | 200 | 230 | 300 |
Dielectric Strength | V/m | 15106 | 15106 | 15106 | 11106 |
Dielectric Phase Angle (1MHz) | 10-4 | 4 | 2 | 1 | 16 |
SIC(1MHz) | | 9.2 | 9.8 | 9.9 | 33 |
Nitric Acid (60%)90C | WT Loss Mg/cm2/day | 0.12 | 0.10 | 0.05 | 0 |
Sodium Hudroxide (30%)80C | WT Loss Mg/cm2/day | 0.53 | 0.26 | 0.04 | 0.08 |
- - - -
96% Alumina Ceramic Substrates (0.8mm)