PA66 GF50(A2011J) - [ Sell Product ]

Place of Origin : Suzhou,China
Post Date : 25-01-2022
Expiry Date : 25-01-2022

Trade Description

PA 66 GF 50 Is A Fiber-reinforced Plastic Made Of Nylon 66 Resin As A Base Material And 50% Glass Fiber As A Reinforcing Filler, And Various Processing Aids Be Added To Be Used In Injection Molding Products.
Typical Application Of PA66GF50(A2011J)
PA66 50%GF HB Grade Is Applied To The Field Of Industrial Product Structural Parts, Requiring High Strength, High Toughness, High And Low-temperature Resistance, And Commonly Used As Water Valve Diverter And Blade Of Air Outlet, Mechanical Gears And Bushings.
Other Details Of PA66 50GF (A2011J)

Physical Property
Ash (50.0% 1 ISO3451/1)
Conditioned 600°C*2h
Density (1538Kg/m3 1 ISO1183)
Conditioned 23°C
Shrinkage Parallel Flow (0.1-0.3 % 1 ISO294-4)
Shrinkage Vertical Flow 0.2-0.5% I ISO294-4)
Mechanical Properties
Tensile Strength (217.0MPa 1 ISO527)
Conditioned 5mm/ Min
Tensile Strain At Break (2.5% I ISO527)
Conditioned 5mm/min
Notched Impact Strength (17.0KJ/m2 I ISO179
Conditioned 1.0J
Flexural Strength (354 MPa 1ISO178)
Conditioned 2mm/min
Flexural Modulus (14263 MPa I ISO178)
Conditioned 2mm/ Min
Thermal Property
Melting Point (260°C I ISO11357)
Hot Deformation Temperature (260*C I ISO75)
Conditioned 1.8MPa
Flammability Class (HB 1UL94)
Conditioned Mm
Injection Molding Conditions
Drying Temperature 130°C
Drying Time 3h
Cylinder Temperature 290-310°C
Nozzle Temperature 290-310*C
Tooling Temperature 80-100*C
* Molding Conditions Are just for Reference, Please Make An Adjustment Based On The Actual Situation!
As A Professional Engineered Plastics Company, Anmei Provide Modified Polyolefin, Pa 6.6 Gf50, Heat Stabilized Nylon And Etc. Want To Know More? Contact Us.