PA66 GF45 Is A 45% Glass Fiber Reinforced Polyamide 6.6 With High Stiffness And Strength.

Typical Application Of PA66 GF45 (A2011I)
PA66 45%GF HB Grade Is Applied To The Gear Field, It Requires High Strength, High Toughness And Dynamic Balance And Applied To The Field Of Sports Equipment And Electrical Tools, It Requires High Toughness, Low Temperature Resistance, And Low Cost. Commonly Used As Mechanical Housing.
Processing Detail Of PA66 GF45 (A2011I)

Other Details Of PA66 GF45 (A2011I)
Physical Property
Ash (45.0% 1 ISO3451/1)
Conditioned 600°C*2h
Density (1495Kg/m3 1 ISO1183)
Conditioned 23°C
Shrinkage Parallel Flow (0.1-0.3% 1 ISO294-4)
Shrinkage Vertical Flow (0.4-0.6% I ISO294-4)
Mechanical Properties
Tensile Strength (204.0MPa 1 ISO527)
Conditioned 5mm/ Min
Tensile Strain At Break (2.8% I ISO527)
Conditioned 5mm/min
Notched Impact Strength (16.5 KJ/m2 IISO179)
Conditioned 1.0J
Flexural Strength (332MPa 1ISO178)
Conditioned 2mm/min
Flexural Modulus (13547 MPa I ISO178)
Conditioned 2mm/min
Thermal Property
Melting Point (260°C I ISO11357)
Hot Deformation Temperature (258*C I ISO75)
Conditioned 1.8MPa
Flammability Class (HB 1UL94)
Conditioned Mm
Injection Molding Conditions
Drying Temperature 130°C
Drying Time 3h
Cylinder Temperature 290-310°C
Nozzle Temperature 290-310*C
Tooling Temperature 80-100*C

* Molding Conditions Are just for Reference, Please Make An Adjustment Based On The Actual Situation!
As A Professional Engineering Plastic Company, Anmei Provide Pa Material, Pa4 6 Gf30, Heat Stabilized Nylon And Etc. Want To Know More? Contact Us.