Inconel 600 (UNS N06600/W.Nr.2.4816) Pipe/Bar/Plate/Ring/Fitting - Product

^{MINIMUM QUANTITY²⁰⁰}

Place of Origin : Jiaxing,China
Delivery Terms : CIF, FOB
Delivery Time : 30
Payment Terms : T/TL/C

Product Description

Chemical composition and minimum mechanical properties :
Alloy % Ni Cr Fe C Mn Si Cu S Al Ti Rp0.2 Rm A 5%
800 Min. 30 19 0.15 0.15 210 500 35
Max. 35 23 balance 0.10 1.5 1 0.75 0.015 0.60 0.60
800H Min. 30 19 0.05 0.15 0.15 180 450 35
Max. 35 23 balance 0.10 1.5 1 0.75 0.015 0.60 0.60
800HT Min. 30 19 0.06 0.15 0.15
Max. 35 23 balance 0.10 1.5 1 0.75 0.015 0.60 0.60
AI+Ti: 0.85-1.20

Incoloy 800H Corrosion resistance:
Excellent corrosion resistance in the hig

Basic Information

Brand : CONFORM
Material : UNSN06600
Color : STEEL
Expiry/Validation Period : LONGTIME

Physical Specification

Other Specification : Chemical Composition And Minimum Mechanical Properties Alloy % Ni Cr Fe C Mn Si Cu P S RP 0.2 Rm A5% 600 Min. 72 14 6 240 550 30 Max. 17 10 0.15 1 0.5 0.5 0.015 0.015 Inconel 600 Characteristic As Below： 1.Good Corrosion Resistance Property For The Reduction, Oxidation, Nitric And Other Media. 2.Good Stress Corrosion Cracking Resistance Property In Both Room Temperature And High Temperature. 3.Good Corrosion Resistance Of The Dry Chlorine And Chlorine Hydride. 4.Good Mechanical Property When Below Zero, Room Temperature And High Temperature. Inconel 600 Application Field1. Erosion Thermocouple Sheath Of The Atmosphere2.Vinyl Chloride Monomer Production: Corrosion Resistance To Chlorine, Hydrogen Chloride, Oxidation And Carbonation. 3. Oxide Shaft Chloride Converted To Six Fluoride: Hydrogen Fluoride Anti-corrosion. 4. Corrosive Alkali Metal Produce And Usage Filed, Especially The Sulfide Use Environment. 5. Use Chlorine Produce Titanium Dioxide6.Organic Or Inorganic Chlorine Produce: Corrosion Resistance To Chlorine And Fluoride. 7. Nuclear Reactor 8.Heat Treatment Furnace Flask And Components, Especially In The Carbonization And Nitride Atmosphere. 8. Petrochemical Works Production Of Catalytic Regeneration In The Application Of More Than 700℃ Recommended The Use Of 600, In Order To Obtain A Longer Service Life.