Ferro Silicon Barium Aluminium Inoculation With FeSi75, FeSiBa with Ca 1.0-2.0%
# # Maximum spheroidization.Encourage type A flake graphite formation in gray irons.
# maxmum chill reduction. Reduced relative hardness to improve machinability.
# Reduced fading tendency.
# reduced sectional sensitivity.
# Stable chemical composition.
# Low melting point(~1300) for easy absorption.
# # Same as other Si base inocuant.
# 0.1-0.5mm is for late stream inoculation.
# Addition