custom 10 AHC impeller investment casting in CF8M or CF3M - Product
Place of Origin : Huizhou,China
Delivery Time : 30days
Product Description
10 AHC impeller investment casting in CF8M or CF3M
Quick Detail:
# Stainless steel CF3M investment castings for impeller of food processing machinery.
# Process: Silica Sol Lost wax casting;
# Wax type: Medium temperature wax;
# Weight: various from 1kg~7kg;
# Finish: Hand polished;
# NDT service available.
Description:
Custom made stainless steel investment casting parts.Investment casting Impeller of food processing machinery,stainless stee
Physical Specification
Other Specification :
10 AHC Impeller Investment Casting In CF8M Or CF3M
Quick Detail:
# Stainless Steel CF3M Investment Castings For Impeller Of Food Processing Machinery.
# Process: Silica Sol Lost Wax Casting;
# Wax Type: Medium Temperature Wax;
# Weight: Various From 1kg~7kg;
# Finish: Hand Polished;
# NDT Service Available.
Description:
Custom Made Stainless Steel Investment Casting Parts.Investment Casting Impeller Of Food Processing Machinery,stainless Steel Casting.
Brife Description Of Investment Casting Process:
# Wax Mold Making: Our Wax Tooling Is Made Of Aluminum Which Is Easy For Machining And Fast For Cooling, At The Same Time, Light For Handling.
# Wax Injection: Feeding The Entire Mould With Molten Wax, And Cool, Until A Desired Wax Pattern Is Shaped And Harden.
# Assemble The Wax Patterns: The Wax Patterns Are Welded To A Runner System By A Heated Metal Tool According To A Certain Pattern Cluster(tree) Design.
# Investment: The Ceramic Mould, Known As The Investment, Is Produced By Three Repeating Steps: Coating, Stuccoing, And Hardening. The First Step Involves Dipping The Cluster Into A Slurry Of Fine Refractory Material And Then Letting Any Excess Drain Off, So A Uniform Surface Is Produced. This Fine Material Is Used First To Give A Smooth Surface Finish And Reproduce Fine Details. In The Second Step, The Cluster Is Stuccoed With A Coarse Ceramic Particle, By Dipping It Into A Fluidised Barrel, Placing It In A Rainfall-sander. Finally, The Coating Is Allowed To Harden.
# Dewax: The Investment Is Then Allowed To Completely Dry, Which Can Take 16 To 48 Hours. It Is Then Turned Upside-down And Placed In A Autoclave To Melt Out And/or Vaporize The Wax.
# Burnout & Preheating: The Mold Is Then Subjected To A Burnout, Which Heats The Mold To Remove Any Moisture And Residual Wax, An