Eco Friendly ED Black Coating Water Based Paint High Anticorrosive Performance - Product
Place of Origin : Shanghai,China
Delivery Time : 30-60 Days
Product Description
High anticorrosive performance black electrophoretic coating ,good corrosin resistance
Product Introduction
HLS-1701ELB/HLS-1701EG Black Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury et
Physical Specification
Other Specification : High Anticorrosive Performance Black Electrophoretic Coating ,good Corrosin Resistance
Product Introduction
HLS-1701ELB/HLS-1701EG Black Cationic Epoxy Electrocoat For Auto Is A New Generation Electrophoretic Coating Researched And Developed By HLS Paint (Shanghai) Co., Ltd. It Represents Modern Technology Of Cathodic Electrophoretic Coating That Is Environment-friendly With High Property And Low Cost. Such Coating Does Not Contain Heavy Metal Like Lead, Tin, Cadmium And Mercury Etc. It Is A Two-component, Water-dispersed Resin,meanwhile, It Took In Features Of Previous Products, And Can Adapt Galvanized Steel Sheet Perfectly, Almost Can Be Applied To Foundation Coating Of All Metal, Such As: Cold And Hot Rolled Steel Sheet, Galvanized Steel Sheet, Aluminum Products, Zinc-aluminum Alloy Sheet And Stainless Steel Sheet Etc.
This Product Features Shown Below:
The Appearance Of The Coating Is Flat, Delicate, Smooth, Uniform High Gloss.
Good Stability Of Bath Can Adaptable For A Longer Updating Cycle.
Etc.
The Main Component Matrix Resin:
Polyurethane Modified Epoxy Resin
Curing Agent: Totally Enclosed Multi-isocyanates
Product Quality Data
- - - -
Project | Technical Data | Test Standard |
Resin
(HLS-1701ELB) | Black Paste(HLS-1701EG) |
Appearance | | Milky White Liquid | Black Viscous Liquid,no Agglomeration | Visual |
PH | 25 | 6.01.0 | | GB/T 9724 |
Conductivity | 25, S/cm | 1400600 | | HG/T 3334 |
Storage Stability |
No Stratified State, And There Were No Obvious Difference Compared To Before Storage | In 5-35 Temperature 1 Year |
- - - -
Note: PH, Conductivity Measurement In The Resin/pure Water = 1:1 Dilution
Filling Tank Proportion And Method
Bath Preparation
Ratio:
Resin 1200.00
Paste 200.00
DI Water