Waterproof Custom Silicone Parts Rubber Cushion With 1.196 G / Cm3

 

Details:

 

Rubber Cushion Productswith The Properties Of Good Flexibility And Anti-compression Deformation, Heat, Oil, Pressure, Acid, Abrasion, Impact Resistance, Tensile Strength, Tear Resistance, Flame, Shock, Cold, Anti-aging.

 

Application:

 

Mainly Used In Automobiles, Motorcycles, Ships, Coal, Electric Power, Metallurgy, Chemical Industry, Mining Equipment And Heavy Machinery Manufacturing And Other Fields.Proof Of Dust, Insects, Water, Fixed, Sound Insulation, Shock Absorption, Sealing And So On..

 

- - - -
Properties Test Report Compound E60D034X ASTM D2000 M2CA610A25B35EA14C32F17 |

Original Properties | SPE Cification | TEST RESULT | ASTM Test Method |
Hardness Shore A | 60°±5 | 58° | D2240 |
Tensile Strength Mpa, Min | 10 | 10.9 | D412 |
Ultimate Elongation %, Min | 250 | 488 | D412 |
Tear Strength (kgf/cm) | 17 | 49 | D624 |
SPE Cific Gravity (g/cm3) | 　 | 1.196 | D297 |
Heat Resistance 70H. AT 125℃ (A25) | 　 | 　 | D865 |
Change In Hardness Points | +10 | +7 | 　 |
Change In Tensile Strength, Max % | -20 | +6.25 | 　 |
Change In Ultimate Elongation % | -40 | -35 | 　 |
Compression Set, Max, 22H. AT 100℃ (B35) | 70 | 51 | D395 Method B |
Water Resistance: 100℃, 70H (EA14) | 　 | 　 | D471 |
Change In Hardness Points | — | -1 | 　 |
Volume Change, % | ±5 | 2 | 　 |
Resistance To Ozone (C32) | No Crack | Pass | D1171 |
Low-temperature, Brittleness (F17) | 　 | 　 | D2137 |
Nonbrittle After 3 Min AT- 40℃ | Nonbrittle | Pass | 　 |
Conclusion: |
Compound E60D034X Can Meet The Requirements Of ASTM D2000 |
M2CA610A25B35EA14C32F17 |
- - - -