Smooth Flat Aluminum Plate Anti-corrosion - Product
Place of Origin : Dongguan,China
Delivery Time : 10~20 Days
Product Description
Smooth Flat Aluminum Plate Anti-corrosion
Specifications
1. Excellent for processing
2. High welding characteristic
3. Good corrosion-resistance
4. High Toughness
5. High polishing
Aluminum flat grade 6061-T6 of size 20~80MM with good oxidation resistance
Applications:
Usedinthemanufactureofheavy dutystructuresrequiringgoodcorrosionresistance,truckandmarinecomponents,
aircraftguncarriage,railroadcars,furniture,tankfittings,generalstructuralandhighpressureapplications,
Physical Specification
Other Specification :
Smooth Flat Aluminum Plate Anti-corrosion
Specifications
1. Excellent For Processing
2. High Welding Characteristic
3. Good Corrosion-resistance
4. High Toughness
5. High Polishing
Aluminum Flat Grade 6061-T6 Of Size 20~80MM With Good Oxidation Resistance
Applications:
Usedinthemanufactureofheavy Dutystructuresrequiringgoodcorrosionresistance,truckandmarinecomponents,
Aircraftguncarriage,railroadcars,furniture,tankfittings,generalstructuralandhighpressureapplications,
Wireproducts,andinpipelines.
Description:
1.Aluminum,Grade:6061,T6orT651
2.Hotrolled,Temper&Pre-stretching,,T651
3.Productionleadtime:25~45days
4.Chemicalcomposition:
- - - -
Si | Mn | Cr | Zn | Mg | Ti | Fe | Cu |
0.40~0.8 | 0.15max | 0.04~0.35 | 0.25 | 0.8~1.2 | 0.15 | 0.7 | 0.15~0.4 |
- - - -
5.Tensilestrength:b(MPa):180
Yieldstrength:0.2(MPa):110
Elongationrate:5(%):14
Machinability:MachinabilityintheharderT4andT6tempersisgood.Itisnotablylesseasytomachinein
Theannealedtemper.
Forming:Easilycoldworkedandformedintheannealedcondition.Stamping,bending,spinning,deepdrawing
Areallreadilyaccomplishedusingstandardmethods.
Welding:Thealloyhasverygoodweldingcharacteristicsandmaybeweldedbyallofthecommonwelding
Techniques.
Gastungstenarcweldingisgenerallyusedforthinsections(lessthan0.032")andgasmetalarcweldingis
Usedforheaviersections.Usealloy4043fillerwireforbestresults,althoughadecreaseinT6propertieswillresult.
HeatTreatment:Solutionheattreatat990Fforadequatetimetoallowforthoroughheatingandthenwaterquench.
Precipitationhardeningisdoneat320Ffor18hoursandaircool,followedby350Ffor8hoursandaircooling.
Forging:Thealloyiscapableofbeinghotforgedattemperaturesintherangeof900Fto750F.
Specifications:
- - - -
Hotrolledcondition | Aluminum Plate(m