Good Refractoriness Fire Clay brick , Carbon Bake Furnaces For The Aluminum Industry - Product
Place of Origin : Qingdao,China
Delivery Time : 20~30 Days
Product Description
Good Refractoriness Fire Clay brick , Carbon Bake Furnaces In The Aluminum Industry
The most competitive price,good quality,safty packing,prompt delivery time,and excellent after-salesservices.
Lower ferric Oxide,lower porosity,higher refractoriness,higher density,higher CCS and exacttolerance.
Specifications:
Technical data
- - - -
Item | SK-30 | SK-32 | SK-34 | SK-36 | SK-38 |
AL2O3% (min) | 30-35% | 35-38% | 38-42% |
Physical Specification
Other Specification :
Good Refractoriness Fire Clay Brick , Carbon Bake Furnaces In The Aluminum Industry
The Most Competitive Price,good Quality,safty Packing,prompt Delivery Time,and Excellent After-salesservices.
Lower Ferric Oxide,lower Porosity,higher Refractoriness,higher Density,higher CCS And Exacttolerance.
Specifications:
Technical Data
- - - -
Item | SK-30 | SK-32 | SK-34 | SK-36 | SK-38 |
AL2O3% (min) | 30-35% | 35-38% | 38-42% | 50-55% | 60-65% |
Fe2O3% (max) | 3 | 3 | 2.8 | 2.5 | 2.3 |
Refractoriness | 1670C | 1690C | 1710C | 1750C | 1770C |
Refractoriness Under Load, 0.2MPa, (C) | 1270 | 1350 | 1350 | 1430 | 1450 |
Apparent Porosity (%) | 20-24 | 20-24 | 19-23 | 18-22 | 18-22 |
Bulk Density (g/cm) | 2.00-2.05 | 2.05-2.1 | 2.1-2.15 | 2.15-2.25 | 2.25-2.35 |
Cold Crushing Strength (MPa) | 25 | 30 | 35 | 45 | 50 |
Thermal Expansion At 1000C (%) | 0.6 | 0.55 | 0.55 | 0.4 | 0.4 |
- - - -
Description:
Laurel Produces A Comprehensive Range Of Fire Clay Brick Consisting Of 30-55% Alumina All Of Which Exhibit Excellent Strength. For More Arduous Environments We Offer A Hand Fired Super Duty Fire Clay Brick With A Very High Mechanical Strength.
Typically Our Firebrick Range Is Based Upon Flint Clay Giving It Both A Low Iron And Low Alkali Characteristic. Resistance To Thermal Shock, Abrasion, Chemical Attack And Reducing Atmospheres Are Just Some Of The Key Criteria Determining Choice Of Product Within Each Application. A Wide Range Of Sizes Are Held In Stock.
Features:
1. Low Thermal Conductivity, Good Thermal Insulation Performance.
2. Long Service Life, Easy Operation, Could Be Shape